--SLA耐熱樹酯--

--耐高溫、抗衝擊、高韌性--

 

熱變形温度Heat distortion temperature:  160℃

玻璃化温度Glass transition temperature:  168℃

 

液態粘度Liquid viscosity:  350-500MPa·s, 25℃/旋轉粘度儀

液態密度Liquid density:  1.05-1.25g/cm3, 25℃/密度計

彎曲模量Flexural modulus:  1.882-2.385 MPa

彎曲强度Bending strength:  60-72MPa

熱膨脹係数Thermal expansion coefficient:  97*E-6

體積收缩率Volume shrinkage:  3.72-4.24%

線收缩率Linear shrinkage:  1.05-1.35%

拉伸强度Tensile Strength:  42-62Mpa

拉伸模量Tensile modulus:  1.86-2.645MPa

斷裂拉伸應變Tensile strain at break:  11%-20%

邵氏硬度Shore Hardness:  85~90

固化後密度Density after curing:  1.09-1.18g/cm2

缺口冲擊强度Notched impact strength:  44-48j/m

最佳儲存温度Optimum storage temperature:  20℃～25℃